Influence of activator concentration on spectral-luminescence and scintillation properties of YAG:Ce crystals

Мұқаба

Дәйексөз келтіру

Толық мәтін

Ашық рұқсат Ашық рұқсат
Рұқсат жабық Рұқсат берілді
Рұқсат жабық Тек жазылушылар үшін

Аннотация

The luminescence and scintillation properties of  YAG:Ce crystals grown from the melts in vacuum has been analysed. We have investigated absorption spectra, X-ray excited luminescence (XRL), XRL decay kinetics and scintillation light yield in a wide range of activator concentrations (from 0.0036 at.% to 1.175 at.% substitution  of  Y in the c-positions of  garnet structure). The effective quenching of the intrinsic luminescence of antisite and vacancy defects of the crystal in the UV region with increasing activator concentration has been determined. The optimal concentration of the activator has been determined in order to increase the XRL intensity and the light output of scintillations of Сe3+ ions, taking into account the technological peculiarities of growing optically perfect single crystals with high concentration of Сe3+ ions by using the method of horizontal directional crystallisation in vacuum. The relations between the XRL kinetics and the activator concentration have been investigated. It has showed the possibility to obtain crystals with photon yield up to 25,000 ph/MeV.

Толық мәтін

Рұқсат жабық

Авторлар туралы

V. Fedorov

Shubnikov Institute of Crystallography of Kurchatov Complex of Crystallography and Photonics of NRC “Kurchatov Institute”

Хат алмасуға жауапты Автор.
Email: fedorov-metrology@yandex.ru
Ресей, Moscow

E. Antonov

Shubnikov Institute of Crystallography of Kurchatov Complex of Crystallography and Photonics of NRC “Kurchatov Institute”

Email: fedorov-metrology@yandex.ru
Ресей, Moscow

I. Venevtsev

Peter the Great St. Petersburg Polytechnic University

Email: fedorov-metrology@yandex.ru
Ресей, St. Petersburg

V. Kanevsky

Shubnikov Institute of Crystallography of Kurchatov Complex of Crystallography and Photonics of NRC “Kurchatov Institute”

Email: fedorov-metrology@yandex.ru
Ресей, Moscow

B. Nabatov

Shubnikov Institute of Crystallography of Kurchatov Complex of Crystallography and Photonics of NRC “Kurchatov Institute”

Email: fedorov-metrology@yandex.ru
Ресей, Moscow

E. Saltanova

Shubnikov Institute of Crystallography of Kurchatov Complex of Crystallography and Photonics of NRC “Kurchatov Institute”; Moscow Institute of Physics and Technology (National Research University)

Email: fedorov-metrology@yandex.ru
Ресей, Москва; Dolgoprudny

Әдебиет тізімі

  1. Kaminskii A.A. Laser Crystals. Springer-Verlag, 1990. 456 p. https://doi.org/10.1007/978-3-540-70749-3_6
  2. Lecoq P., Gektin A., Korzhik M. Inorganic scintillators for detector systems. Switzerland: Springer, 2017. 408 p. https://doi.org/10.1007/978-3-319-45522-8_1
  3. Петросян А.Г. Физика и спектроскопия лазерных кристаллов / Под ред. Каминского А.А. М.: Наука, 1986. 235 с.
  4. Багдасаров Х.С. Высокотемпературная кристаллизация из расплава. М.: Физматлит, 2004. 160 с.
  5. Zhaoa G., Zenga X., Xua J. et al. // J. Cryst. Growth. 2003. V. 253. P. 290. https://doi.org/10.1016/S0022-0248(03)01017-0
  6. Зоренко Ю.В., Савчин В.П., Горбенко В.И. и др. // ФТТ. 2011. Т. 53. Вып. 8. С. 1542.
  7. Нижанковский С.В., Данько А.Я., Зеленская О.В. и др. // Письма в ЖТФ. 2009. Т. 35. Вып. 20. С. 77.
  8. Ashurov M.Kh., Voronko Yu.K., Osiko V.V., Sobol A.A. // Phys. Status Solidi. A. 1977. V. 42. P. 101.
  9. Zorenko Y., Zorenko T., Gorbenko V.V. et al. // Opt. Mater. 2012. V. 34. № 8. P. 1314. https://doi.org/10.1016/j.optmat.2012.02.007
  10. Zorenko Y. // Phys. Status Solidi. C. 2005. V. 2. № 1. P. 375. https://doi.org/10.1002/pssc.200460275
  11. Shiran N., Gektin A., Gridin S. et al. // IEEE Trans. Nucl. Sci. 2018. V. 65. № 3. P. 871. https://doi.org/10.1109/TNS.2018.2797545
  12. Khanin V.M., Vrubel I.I., Polozkov R.G. et al. // J. Phys. Chem. C. 2019. V. 123. № 37. P. 22725. https://doi.org/10.1021/acs.jpcc.9b05169
  13. Zorenko Yu., Zych E., Voloshinovskii A. // Opt. Mater. 2009. V. 31. P. 1845. https://doi.org/10.1016/j.optmat.2008.11.026
  14. Pankratov V., Grigorjeva L., Millers D., Chudoba T. // Radiat. Meas. 2007. V. 42. № 4–5. P. 679. https://doi.org/10.1016/j.radmeas.2007.02.046
  15. Waetzig K., Kunzer M., Kinski I. // J. Mater. Res. 2014. V. 29. № 19. P. 2318. https://doi.org/10.1557/jmr.2014.229
  16. Кварталов В.Б., Федоров В.А., Буташин А.В., Каневский В.М. // Успехи в химии и химической технологии. 2022. Т. 36. № 7. С. 70.
  17. Rodnyi P.A., Mikhrin S.B., Mishin A.N., Sidorenko A.V. // IEEE Trans. Nucl. Sci. 2001. V. 48. № 6. P. 2340. https://doi.org/10.1109/23.983264
  18. Zorenko Y., Zorenko T., Gorbenko V.V. et al. // Opt. Mater. 2012. V. 34. № 8. P. 1314. https://doi.org/10.1016/j.optmat.2012.02.007
  19. Zorenko Yu., Voloshinovskii A., Savchyn V. et al. // Phys. Status Solidi. B. 2007. V. 244. P. 2180. https://doi.org/10.1002/pssb.200642431
  20. Bachmann V., Ronda C., Meijerink A. // Chem. Mater. 2009. V. 21. P. 2077. https://doi.org/10.1021/cm8030768
  21. Zorenko Y., Gorbenko V., Mihokova E. et al. // Radiat. Meas. 2007. V. 42. P. 521. https://doi.org/10.1016/j.radmeas.2007.01.045
  22. Khanin V., Venevtsev I., Spoor S. et al. // Opt. Mater. 2017. V. 72. P. 161. https://doi.org/10.1016/j.optmat.2017.05.040
  23. Zorenko Y., Voloshinovskii A., Savchyn V. et al. // Phys. Status Solidi. B. 2007. V. 244. № 6. P. 2180. https://doi.org/10.1002/pssb.200642431
  24. Буташин А.В., Веневцев И.Д., Федоров В.А. и др. // Кристаллография. 2023. T. 68. № 4. С. 594. https://doi.org/10.31857/S0023476123600234

Қосымша файлдар

Қосымша файлдар
Әрекет
1. JATS XML
Жүктеу
2. Fig. 1. Absorption spectra of IAG crystal samples:Ce thickness d: 6 – d = 690, 7 – d = 443, 9 – d = 37, 12 – d = 65 microns. The curve numbers correspond to the sample numbers from Table 1

Жүктеу (118KB)
Метадеректер
3. Fig. 2. RL spectra of YAG:Ce crystals. The curve numbers correspond to the sample numbers from Table 1

Жүктеу (200KB)
Метадеректер
4. Fig. 3. Dependence of the RL intensity of IAG crystals:Ce at a wavelength of λ = 560 nm of crystals from the concentration of the activator: 1 – crystals grown by the GNC method, 2 – crystals obtained by spontaneous crystallization

Жүктеу (64KB)
Метадеректер
5. Fig. 4. Dependences of the RF intensity at the wavelength λ = 560 nm of the YAG:Ce samples on time. The curve numbers correspond to the sample numbers from Table 1.

Жүктеу (289KB)
Метадеректер
6. Fig. 5. Dependence of the integral contribution of various components of the kinetics of RL of IAG samples:Ce of cerium concentration: 1 – component 68 ns, 2 – component 1090 ns, 3 – intermediate component (190 ns)

Жүктеу (107KB)
Метадеректер
7. Fig. 6. Dependence of the light output of scintillations of IAG crystals:Ce depends on the concentration of the activator: 1 – light output of Ce3+ ions, 2 – light output of the base; a – crystals grown by the GNC method, b – crystals obtained by spontaneous crystallization

Жүктеу (120KB)
Метадеректер

© Russian Academy of Sciences, 2024